E71T-1C

E71T-1C


Flux Cored welding Wire E71T-1C AWS SPECIFICATION: AWS A5.20 ASME SFA-A5.20 Typical Applications: • Pipeline • Offshore structure • Pressure vessel • Structural parts of carbon steel and low alloy……


Описание продукции
Flux Cored welding Wire E71T-1C

AWS SPECIFICATION: AWS A5.20 ASME SFA-A5.20


Typical Applications:

• Pipeline

• Offshore structure

• Pressure vessel

• Structural parts of carbon steel and low alloy structural steel with tensile strength ≥
490 MPA is the most widely used

Features:

• E71T-1 flux core MIG wire GMAW (MIG) welding alloy
• Designed for welding heat-treatable base alloys
• Suitable for sustained elevated temperature service
• All positions, include vertical down welding
• Gray-white(post anodized) color

Welding Current: (DCEN) Straight Polarity

Welding Positions: H, F, V-up, O

Shielding Gas: 100% CO2

Performance Characteristics:

• E71T-1 is titanium oxide type CO2 gas shielded flux cored wire with excellent welding

performance and soft and stable arc.

• Small splash, easy slag removal, beautiful welding seam. Suitable for all
position of welding, the welding efficiency is high.

• The weld metal is treated with trace elements and has good low – temperature toughness, good
crack resistance and stable and reliable intrinsic quality.

E71T-1C

Available Sizes:

Diameter

mm

Spool

5kg

Spool

15kg

1.2
1.4
1.6

Mechanical Properties of Deposited Metal

Test Item Rm(N/mm2) Rel/Rpo.2(N/mm2) A (%) KV2(J)-20℃
Guarantee Value ≧480 ≧400 ≧22 ≧27
General Result 560 480 28 129

Reference Current (DC)

Diameter(mm) 1.2 1.4 1.6
Current(A) F 120-300 150-380 180-430
HF 120-280 150-320 180-380
V, OH 120-260 150-270 180-280
H 120-280 150-320 180-330
VD 200-280 220-300 250-300

Notice:

1. The flow rate of shield gas should be within 20L-25L/min

2. The wire extension should be 15mm-25mm.

3. The surfaces to be welded must be cleaned away from impurities of oil contamination, rust, moisture, and so on.

4. The welding conditions mentioned above are for reference only and it is better to do a welding procedure qualification according to the project before putting it into formal welding

Mechanical Properties of Deposited Metal(AW)

Yield Point

ReH(Mpa)

Tensile Strength

Rm(Mpa)

Elongation

A4(%)

Impact Value(J) Shield Gas
-20℃ Co2
Standard ≥410 ≥500 ≥22 ≥47 purity 99 98 ≥.%
Typical 550 585 27 80